In the thesis CuPc thin films were investigated by (in situ) SE and RAS, which are employed to determine the out-of-plane and in-plane optical anisotropy and molecular orientation, respectively. CuPc is a promising candidate of organic semiconductors used in organic field effect transistors, organic light emitting diodes and organic solar cells. Vicinal Si(111) substrates are interesting due to the in-plane anisotropy caused by the steps and terraces on the surface. The strength of in-plane anisotropy of vicinal Si(111) is dependent on the offcut angle. The influence of offcut angle on out-of-plane and in-plane molecular orientation in CuPc thin films is explored. The in situ investigation of CuPc films suggests that structural changes occur during film growth. In addition, two different surface modification layers were utilized to examine the effect on CuPc molecular orientation: OTS monolayer with upright standing molecules and PTCDA layers with flat lying molecules. Metal-organic interface plays an important role in organic electronic devices. In-CuPc is chosen to be an example system investigated employing in situ SE and RAS. When In was thermally evaporated onto CuPc film, In atoms firstly diffuse into the CuPc film underneath and then aggregate to form clusters on top. Hafnium dioxide (HfO2) is currently a hot topic to replace the conventionally used SiO2 as gate dielectrics in order to minimize leakage current when further scaling down microelectronic devices. Since HfO2 films are often crystalline, in order to obtain amorphous films which are beneficial to minimize leakage current, aluminum oxide (Al2O3) (k value: 9) which stays amorphous at much higher temperatures are combined to overcome this difficulty. Two series of ultra-thin samples were deposited by atomic layer deposition: mixed layers HfxAl1-xOz and bilayers HfO2 on Al2O3. Optical constants and bandgap are determined using SE in the energy range of 0.7-10 eV. It is found that the (effective) optical bandgap of both mixed layer and bilayer structures can be tuned by the film composition. Aging effect of high-k films was observed after storage of samples in air for two months, which is attributed to further oxidation of the dielectric films caused by the oxygen diffusion from ambient air to high-k films. In dieser Arbeit werden dünne Schichten aus Kupferphthalozyanin (CuPc) mittels spektroskopischer (in-situ) Ellipsometrie (SE) und (in-situ) Reflektions-Anisotropie-Spektroskopie (RAS) untersucht, um die optische Anisotropie in einer Ebene parallel und senkrecht zur Schichtoberfläche und die molekulare Orientierung zu bestimmen. CuPc ist ein aussichtsreicher Kandidat als organischer Halbleiter in organischen Feldeffekt-Transistoren, organischen Leuchtdioden und organischen Solarzellen. Vizinale Si(111)-Substrate sind wegen der Anisotropie in der Substratebene interessant, die durch die Treppen und Terrassen auf der Oberfläche verursacht wird. Die Stärke der Anisotropie der vizinalen Si(111)-Oberfläche ist vom Schnittwinkel (Offcut) abhängig. Es…